Low-tack ophthalmic and otorhinolaryngological device materials

ABSTRACT

Disclosed are soft, high refractive index, acrylic materials. These materials, especially useful as intraocular lens materials, contain an aryl acrylic hydrophobic monomer as the single principal device-forming monomer and a tack-reducing macromer additive. In addition to their use as intraocular lens materials, the present materials are also suitable for use in other ophthalmic or otorhinolaryngological devices, such as contact lenses, keratoprostheses, corneal inlays or rings; otological ventilation tubes and nasal implants.

This application claims priority to U.S. Provisional Application, U.S. Ser. No. 60/832,478 filed Jul. 21, 2006.

FIELD OF INVENTION

This invention is directed to acrylic device materials. In particular, this invention relates to low-tack, high refractive index acrylic device materials particularly suited for use as intraocular lens (“IOL”) materials.

BACKGROUND OF INVENTION

With the recent advances in small-incision cataract surgery, increased emphasis has been placed on developing soft, foldable materials suitable for use in artificial lenses. In general, these materials fall into one of three categories: hydrogels, silicones, and acrylics.

In general, hydrogel materials have a relatively low refractive index, making them less desirable than other materials because of the thicker lens optic necessary to achieve a given refractive power. Silicone materials generally have a higher refractive index than hydrogels, but tend to unfold explosively after being placed in the eye in a folded position. Explosive unfolding can potentially damage the corneal endothelium and/or rupture the natural lens capsule. Acrylic materials are desirable because they typically have a higher refractive index than silicone materials and unfold more slowly or controllably than silicone materials.

U.S. Pat. No. 5,290,892 discloses high refractive index, acrylic materials suitable for use as an IOL material. These acrylic materials contain, as principal components, two aryl acrylic monomers. They also contain a cross-linking component. The IOLs made of these acrylic materials can be rolled or folded for insertion through small incisions.

U.S. Pat. No. 5,331,073 also discloses soft acrylic IOL materials. These materials contain as principal components, two acrylic monomers which are defined by the properties of their respective homopolymers. The first monomer is defined as one in which its homopolymer has a refractive index of at least about 1.50. The second monomer is defined as one in which its homopolymer has a glass transition temperature less than about 22° C. These IOL materials also contain a cross-linking component. Additionally, these materials may optionally contain a fourth constituent, different from the first three constituents, which is derived from a hydrophilic monomer. These materials preferably have a total of less than about 15% by weight of a hydrophilic component.

U.S. Pat. No. 5,693,095 discloses foldable ophthalmic lens materials comprising a total of at least 90% by weight of only two principal lens-forming monomers. One lens-forming monomer is an aryl acrylic hydrophobic monomer. The other lens-forming monomer is a hydrophilic monomer. The lens materials also comprise a cross-linking monomer and optionally comprise a UV absorber, polymerization initiators, reactive UV absorbers and reactive blue-light absorbers.

U.S. Pat. No. 6,653,422 discloses foldable ophthalmic lens materials consisting essentially of a single device-forming monomer and at least one cross-linking monomer. The materials optionally contain a reactive UV absorber and optionally contain a reactive blue-light absorber. The single device-forming monomer is present in an amount of at least about 80% by weight. The device-forming monomer is an aryl acrylic hydrophobic monomer.

Some foldable acrylic materials are tacky. Foldable ophthalmic lenses made of tacky acrylic materials are difficult to handle. Attempts have been made to reduce tackiness so that the lenses are easier to process or handle, easier to fold or deform, and have shorter unfolding times. For example, U.S. Pat. No. 6,713,583 discloses ophthalmic lenses made of a material that includes branched chain alkyl groups in an amount effective to reduce tackiness. U.S. Pat. No. 4,834,750 discloses intraocular lenses made from materials that optionally include a fluoroacrylate component to reduce surface tackiness. U.S. Pat. No. 5,331,073 discloses acrylic materials that optionally include a hydrophilic component that is present in an amount sufficient to reduce the materials' tackiness. U.S. Pat. No. 5,603,774 discloses a plasma treatment process for reducing the tackiness of a soft acrylic article.

SUMMARY OF THE INVENTION

Improved soft, foldable acrylic materials which are particularly suited for use as IOLs, but which are also useful as other ophthalmic or otorhinoloaryngological devices, such as contact lenses, keratoprostheses, corneal rings or inlays, otological ventilation tubes and nasal implants have now been discovered. These materials contain only one principal lens-forming component, an aryl acrylic hydrophobic monomer, in an amount of at least about 75% by weight. The materials also contain a macromer additive in an amount sufficient to reduce the materials' tackiness. The macromer additive is a dimethylacryloxypropyl-terminated polydimethylsiloxane macromer. The remainder of the material comprises a cross-linking monomer and optionally one or more additional components selected from the group consisting of UV-light absorbing compounds and blue-light absorbing compounds.

DETAILED DESCRIPTION OF THE INVENTION

The ophthalmic or otorhinolaryngological device materials of the present invention comprise only one principal device-forming monomer. For convenience, the device-forming monomer may be referred to as a lens-forming monomer, particularly with reference to an IOL. The materials of the present invention, however, are also suitable for use as other ophthalmic or otorhinolaryngological devices such as contact lenses, keratoprostheses, corneal inlays or rings, otological ventilation tubes and nasal implants.

The aryl acrylic hydrophobic monomers suitable for use as the principal lens-forming monomer in the materials of the present invention have the formula

wherein: A is H, CH₃, CH₂CH₃, or CH₂OH;

-   -   B is (CH₂)_(m) or [O(CH₂)₂]_(n);     -   C is (CH₂)_(w);     -   m is 2-6;     -   n is 1-10;     -   Y is nothing, O, S, or NR, provided that if Y is O, S, or NR,         then B is (CH₂)_(m);     -   R is H, CH₃, C_(n)H_(2n+1) (n=1-10), iso-OC₃H₇, C₆H₅, or         CH₂C₆H₅;     -   w is 0-6, provided that m+w≦8; and     -   D is H, C₁-C₄ alkyl, C₁-C₄ alkoxy, C₆H₅, CH₂C₆H₅ or halogen.

Preferred aryl acrylic hydrophobic monomers for use in the materials of the present invention are those wherein A is CH₃, B is (CH₂)_(m), m is 2-5, Y is nothing or O, w is 0-1, and D is H. Most preferred are 4-phenylbutyl methacrylate, 5-phenylpentyl methacrylate, 2-benzyloxyethyl methacrylate, and 3-benzyloxypropyl methacrylate.

Monomers of structure I can be made by known methods. For example, the conjugate alcohol of the desired monomer can be combined in a reaction vessel with methyl methacrylate, tetrabutyl titanate (catalyst), and a polymerization inhibitor such as 4-benzyloxy phenol. The vessel can then be heated to facilitate the reaction and distill off the reaction by-products to drive the reaction to completion. Alternative synthesis schemes involve adding methacrylic acid to the conjugate alcohol and catalyzing with a carbodiimide or mixing the conjugate alcohol with methacryloyl chloride and a base such as pyridine or triethylamine.

The materials of the present invention comprise a total of at least about 75%, preferably at least about 80%, by weight or more of the principal lens-forming monomer.

In addition to the principal lens-forming monomer, the materials of the present invention contain a macromer additive in an amount sufficient to reduce the material's tackiness. Generally, the amount of macromer additive in the materials of the present invention will range from 0.5-3.9% (w/w), and preferably will range from 0.5-2% (w/w), most preferably 0.8-1.2% (w/w). The macromer is a dimethylacryloxypropyl-terminated polydimethylsiloxane macromer of the formula:

wherein

-   R₁ and R₂ are independently —CH₃, —CH₂CH₃, —CH₂CH₂CH₂CH₃,     CH₂CH₂CH₂CH₃, —C₆H₅, —CH₂C₆H₅, —CH₂CH₂C₆H₅, —CH₂CH₂CH₂C₆H₅, or     —CH₂CH₂CH₂CH₂C₆H₅; -   R₃ is H, CH₃, or CH₂CH₃; -   z is 2-11; and -   x indicates the number of repeating units and determines the     molecular weight of the macromer.

Preferred macromers are those wherein

-   R₁═R₂═CH₃; -   R₃ is H, CH₃, or CH₂CH₃; and -   z=3; and -   x=0-43.

More preferred macromers are those wherein R₁, R₂, R₃, and z are as defined above for the preferred macromers and x is 0-22. In one embodiment, x is 5-14 (generally corresponding to a macromer molecular weight (M_(n)) of 800-1400). In another embodiment, x is 2-5 (generally corresponding to a macromer molecular weight (M_(n)) of 550-700).

Dimethylacryloxypropyl-terminated polydimethylsiloxanes of the above formula (“PDMS”), also known as methacryloxypropyl terminated polydimethyl siloxanes, can be made by known methods. Some PDMS compounds are commercially available from Gelest, Inc. in molecular weights (M_(n)) ranging from 800-1400 (mid-range M_(n) estimated as 1000). There are higher (M_(n) 4K-6K, 5K-20K, 20K -30K) and lower (M_(n) 386, 550-700) molecular weight grades of dimethacryloxypropyl-terminated siloxane commercially available. The macromer additive selection is limited by solubility (in the remainder of the copolymer material formulation) and formulation clarity (the copolymer material should be clear). Generally, PDMS used in the present invention will have a molecular weight (M_(n)) of about 300-about 3500 and preferably about 350-about 2000. In one embodiment, an especially preferred PDMS has a M_(n) from about 800-about 1400. In another embodiment, an especially preferred PDMS has a M_(n) from about 550-about 700.

The copolymer materials of the present invention are cross-linked. The copolymerizable cross-linking agent used in the copolymers of this invention may be any terminally ethylenically unsaturated compound having more than one unsaturated group. Suitable cross-linking agents include, for example: ethylene glycol dimethacrylate; diethylene glycol dimethacrylate; allyl methacrylate; 1,3-propanediol dimethacrylate; 2,3-propanediol dimethacrylate; 1,6-hexanediol dimethacrylate; 1,4-butanediol dimethacrylate; CH₂═C(CH₃)C(═O)O—(CH₂CH₂O)_(p)—C(═O)C(CH₃)═CH₂ where p=1-50; and CH₂═C(CH₃)C(═O)O(CH₂)_(t)O—C(═O)C(CH₃)═CH₂ where t=3-20; and their corresponding acrylates. A preferred cross-linking monomer is CH₂═C(CH₃)C(═O)O—(CH₂CH₂O)_(p)—C(═O)C(CH₃)═CH₂ where p is such that the number-average molecular weight is about 400, about 600, or about 1000. The most preferred cross-linking agent is CH₂═C(CH₃)C(═O)O—(CH₂CH₂O)_(p)—C(═O)C(CH₃)═CH₂ where p is such that the number-average molecular weight is about 1000 (“PEG(1000)DMA”).

The chosen cross-linking agent should be soluble in the chosen monomer of structure I to minimize curing problems. When p approaches the upper end of the range of 1-50, the CH₂═C(CH₃)C(═O)O—(CH₂CH₂O)_(p)—C(═O)C(CH₃)═CH₂ cross-linker may not be soluble at desired levels in some monomers of structure I, even with the aid of heat or sonication.

Generally, only one cross-linking monomer will be present in the device materials of the present invention. In some cases, however, combinations of cross-linking monomers may be desirable. A preferred combination of cross-linking monomers is PEG(1000)DMA and ethylene glycol dimethacrylate (“EGDMA”).

Generally, the total amount of the cross-linking component is at least 0.1% by weight and, depending on the identity and concentration of the remaining components and the desired physical properties, can range to about 20% by weight. The preferred concentration range for the cross-linking component is 0.1-17% (w/w).

In addition to the aryl acrylic hydrophobic lens-forming monomer, the macromer additive, and the cross-linking component, the lens material of the present invention may also contain a total of up to about 10% by weight of additional components which serve other purposes, such as reactive UV and/or blue-light absorbers.

Preferred reactive UV absorbers are 2-(2′-hydroxy-3′-methallyl-5′-methylphenyl)benzotriazole, commercially available as o-Methallyl Tinuvin P (“oMTP”) from Polysciences, Inc., Warrington, Pa., and 2-[3-(2H-benzotriazol-2-yl)-4-hydroxyphenylethyl]methacrylate (“BHMA”). UV absorbers are typically present in an amount from about 0.1-5% (w/w).

Suitable reactive blue-light absorbing compounds are those described in U.S. Pat. No. 5,470,932, the entire contents of which are hereby incorporated by reference. Blue-light absorbers are typically present in an amount from about 0.01-0.5% (w/w).

Suitable polymerization initiators include thermal initiators and photoinitiators. Preferred thermal initiators include peroxy free-radical initiators, such as t-butyl (peroxy-2-ethyl)hexanoate and di-(tert-butylcyclohexyl)peroxydicarbonate (commercially available as Perkadoxe® 16 from Akzo Chemicals Inc., Chicago, Ill.). Particularly in cases where the lens material does not contain a blue-light absorbing chromophore, preferred photoinitiators include benzoylphosphine oxide photoinitiators, such as the blue-light initiator 2,4,6-trimethyl-benzoyidiphenylphosphine oxide, commercially available as Lucirin® TPO from BASF Corporation (Charlotte, N.C.). Initiators are typically present in an amount of about 5% (w/w) or less. Because free-radical initiators do not become chemically a part of the polymers formed, the total amount of initiator is customarily not included when determining the amounts of other ingredients.

The identity and amount of the principal lens-forming monomer described above and the identity and amount of any additional components are determined by the desired properties of the finished ophthalmic lens. Preferably, the ingredients and their proportion are selected so that the acrylic lens materials of the present invention possess the following properties, which make the materials of the present invention particularly suitable for use in IOLs which are to be inserted through incisions of 5 mm or less.

The lens material preferably has a refractive index in the dry state of at least about 1.50 as measured by an Abbe' refractometer at 589 nm (Na light source). For a given optic diameter, optics made from materials having a refractive index lower than 1.50 are necessarily thicker than optics of the same power which are made from materials having a higher refractive index. As such, IOL optics made from materials having a refractive index lower than about 1.50 generally require relatively larger incisions for IOL implantation.

The glass-transition temperature (“Tg”) of the lens material, which affects the material's folding and unfolding characteristics, is preferably below about 25° C., and more preferably below about 15° C. Tg is measured by differential scanning calorimetry at 10° C./min., and is determined as the half-height of the heat capacity increase.

The lens material will have an elongation (strain at break) of at least 75%, preferably at least 90%, and most preferably at least 100%. This property indicates that the lens generally will not crack, tear or split when folded. Elongation of polymer samples is determined on dumbbell shaped tension test specimens with a 20 mm total length, length in the grip area of 11 mm, overall width of 2.49 mm, 0.833 mm width of the narrow section, a fillet radius of 8.83 mm, and a thickness of 0.9 mm. Testing is performed on samples at standard laboratory conditions of 23±2° C. and 50±5% relative humidity using a tensile tester. The grip distance is set at 11 mm and a crosshead speed is set at 500 mm/minute and the sample is pulled to failure. The strain at break is reported as a fraction of the displacement at failure to the original grip distance. Stress at break is calculated at the maximum load for the sample, typically the load when the sample breaks, assuming that the initial area remains constant. The Young's modulus is calculated from the instantaneous slope of the stress-strain curve in the linear elastic region. The 25% secant modulus is calculated as the slope of a straight line drawn on the stress-strain curve between 0% strain and 25% strain. The 100% secant modulus is calculated as the slope of a straight line drawn on the stress-strain curve between 0% strain and 100% strain.

IOLs constructed of the materials of the present invention can be of any design capable of being rolled or folded into a small cross section that can fit through a relatively smaller incision. For example, the IOLs can be of what is known as a one piece or multipiece design, and comprise optic and haptic components. The optic is that portion which serves as the lens. The haptics are attached to the optic and hold the optic in its proper place in the eye. The optic and haptic(s) can be of the same or different material. A multipiece lens is so called because the optic and the haptic(s) are made separately and then the haptics are attached to the optic. In a single piece lens, the optic and the haptics are formed out of one piece of material. Depending on the material, the haptics are then cut, or lathed, out of the material to produce the IOL.

The invention will be further illustrated by the following examples, which are intended to be illustrative, but not limiting.

EXAMPLE 1 Synthesis of 4-phenylbutyl methacrylate (“PBMA”)

A three neck round bottom flask containing a teflon coated magnetic stirring bar was successively charged with 120 mL (1.09 mol) of methyl methacrylate (2), 5.35 g (0.015 mol) of titanium tetrabutoxide (Ti(OC₄H₉)₄), 60 mL (0.39 mol) of 4-phenyl-1-butanol (1), and 14.6 g (0.073 mol) of 4-benzyloxyphenol (4-BOP). An addition funnel, thermometer, and a short path still head with thermometer and receiver flask were placed in the flask necks. The flask was placed in an oil bath and the temperature was increased until distillation began. Methyl methacrylate (2) was placed in the addition funnel and was added dropwise at the same rate as the distillate. The reaction mixture was heated for 4 hours and then cooled to room temperature. The crude product was vacuum distilled to isolate 62.8 g (0.29 mol, 74%) of 4-phenylbutyl methacrylate (3) as a clear, colorless liquid.

EXAMPLE 2 Synthesis of 3-benzyloxypropyl methacrylate

A three neck round bottom flask containing a teflon coated magnetic stirring bar was successively charged with 95 mL (0.884 mol) of methyl methacrylate (2), 4.22 g (0.012 mol) of titanium tetrabutoxide (Ti(OC₄H₉)₄), 50 mL (0.316 mol) of 3-benzyloxy-1-propanol (1), and 14.6 g (0.073 mol) of 4-benzyloxyphenol (4-BOP). An addition funnel, thermometer, and a short path still head with thermometer and receiver flask were placed in the flask necks. The flask was placed in an oil bath and the temperature was increased until distillation began. Methyl methacrylate (2) was placed in the addition funnel and was added dropwise at the same rate as the distillate. The reaction mixture was heated for 4 hours and then cooled to room temperature. The crude product was vacuum distilled to isolate 36.5 g (0.156 mol, 49%) of 3-benzyloxypropyl methacrylate (3) as a clear, colorless liquid.

EXAMPLE 3 Preferred Intraocular Lens Material

A preferred intraocular lens material is presented below. All amounts are expressed as % by weight. This formulation can be initiated with a peroxy free-radical initiator, such as 1% di-(4-t-butylcyclohexyl)peroxydicarbonate (“PERK16S”)

Ingredient % (w/w) PBMA 82-84 PDMS (MW = 800-1400) 0.5-2   PEG(1000)DMA 13-15 EGDMA 1 UV absorber 0.1-5   Blue-light absorber 0.01-0.5 

The chemicals are weighed, mixed, and filtered together. The resulting formulation solution is flushed with nitrogen gas and then transferred to a glovebox with a low oxygen atmosphere. The formulation is pipetted into degassed polypropylene molds. The assembled molds are then transferred to an oven and cured at 90° C. for 1 hour, followed by a post-cure at 110° C. for 1 hour. The polymer samples are removed from the molds after cooling. The low tack property of the samples is noticeable at this step of the preparation. The samples are extracted with acetone and vacuum dried. Subsequent tack evaluations show the materials are less tacky than control samples not containing PDMS.

EXAMPLES 4-10

Each of the formulations of Examples 4-10 was prepared as follows. In each case, the “PDMS” was dimethylacryloxypropyl-terminated polydimethylsiloxane (R₁═R₂═R₃═CH₃, and z=3).

Monomers were weighed into amber glass scintillation vials with teflon-lined screw-caps. The vials are shaken 1 hr on an orbital shaker until the liquid PDMS formed a uniform, clear solution. Then the initiator was added to the sample in an amount equal to about 1% of the total formulation weight. The initiator for each sample was PERK16S. After filtering the sample through a 1-micron glass fiber membrane syringe filter connected to a 5-mL latex-free, oil-free syringe, the formulation was purged with nitrogen for 5-15 min and then capped to keep out air. Samples were cast into polypropylene slab or lens molds in a glovebox (a containment device which provides a microenvironment of a dry nitrogen atmosphere with less than 50-140 ppm oxygen). To maintain the mold geometry during curing, spring clamps are used on the slab molds. The slab and lens molds were previously prepared by heating at 90° C. for more than 2 hrs. under vacuum (less than 0.1 in Hg pressure), then transferring the molds to the glovebox. After filling the molds, the samples were transferred from the glove box to a curing oven and heated for 1 hr. at 90° C., followed by 1 hr. at 110° C. The samples were cooled to room temperature and then stored briefly in the freezer before opening the molds. After opening the molds, the cured samples were extracted in acetone to remove any materials not bound to the cross-linked network and then dried in air. Finally, the samples were placed into polypropylene tissue capsules and then into a vacuum oven and dried under vacuum at 60-63° C. and below 0.1 inches Hg pressure. The samples were inspected visually to record whether they were clear.

Physical property data labeled “Stress at Break, “Strain at Break”, “Young's Modulus,” “25% Secant Modulus,” and “100% Secant Modulus” in the tables below was assessed according to the methods referred to above. “Quantitative Tack” was determined by the following method. The tack testing apparatus has two parts: a bottom component attached to the lower stationary Instron grip and a top component attached to the upper movable Instron grip. At the center of the bottom component is a 4-mm diameter cylindrical stainless steel stage attached on its end and thus standing vertical. Testing specimens are placed on the exposed end of the stage which is finely polished to mimic the finish on most stainless steel surgical instruments. The top component contains a 4.1-mm diameter circular opening that slides over the cylindrical stage as the top component is lowered. During testing, the upper component is raised and the edges of the circular opening contact the specimen and detach it from the cylindrical stage. In preparation for testing, the tack testing apparatus is mechanically fixed to an Instron testing instrument. Test specimens are prepared by punching 6-mm disks out of polymer slabs with a die. Prior to each experimental run, the upper component of the apparatus is lowered so it is just below the top of the 5-mm diameter polished stainless steel cylindrical stage at the center of the base. It is important to verify that no part of the upper component in any way contacts the cylinder. If any contact occurs, it will register a load during testing due to frictional forces and negatively impact the quality of the results. Once the top is set in place, a polymer disk is placed on the stage, and a 50-g weight is then placed on the disk. After a one-minute equilibration time, the run is started. The testing method simply consists of raising the upper component of the apparatus at a constant rate of 10 mm/min until the disk is fully separated from the cylinder. To maintain a clean and consistent contact surface, the lower stage is cleaned with acetone and allowed to fully dry between samples. A load-displacement curve is generated for each run. This curve is used for calculating the energy (“Tack: Total Energy”) required to detach the sample from the cylinder. Detachment energy is determined by calculating the area under the load-displacement curve. Qualitative observations were obtained by handling the samples with metal forceps (“Tackiness by Handling”).

Unless indicated otherwise, all ingredient amounts shown below are listed as % (w/w). The following abbreviations are used in Tables 1-4:

PBMA: 4-phenylbutylmethacrylate

PDMS: dimethacryloxypropyl-terminated polydimethylsiloxane

PEG(1000)DMA: polyethylene glycol 1000 dimethacrylate

EGDMA: ethylene glycoldimethacrylate

BHMA: 2-[3-(2H-benzotriazol-2-yl)-4-hydroxyphenylethyl]methacrylate.

TABLE 1 INGREDIENT CONTROL EX. 4 PBMA 83.99 83.98 PDMS (MW = 800-1400) —  2.01 PEG(1000) DMA 15.00 12.99 EGDMA  1.01  1.02 Tack: Total Energy (mJ) 2.01 ± 0.24 0.62 ± 0.23 Tackiness by Handling Tacky Slightly tacky Appearance (dry) Clear Clear Appearance (in water @ 35° C.) N/A Clear

TABLE 2 INGREDIENT CONTROL EX. 5 EX. 6 EX. 7 PBMA 82.99 80.99  81.98  82.50  PDMS (MW = 800-1400) — 2.01 1.02 0.50 PEG (1000) DMA 15.01 15.00  15.00  14.99  EGDMA  0.99 1.00 1.00 1.00 BHMA  1.00 1.01 1.01 1.01 Tack: Total Energy (mJ) 1.47 ± 0.34 0.31 ± 0.06 0.55 ± 0.16 1.12 ± 0.35 Appearance (dry) Clear Clear Clear Clear Stress @ break (mPa) 4.97 ± 0.48 5.29 ± 0.46 5.69 ± 0.78 5.11 ± 0.43 Strain @ break (%) 102.4 ± 4.7  102.1 ± 5.8  107.0 ± 8.3  102.0 ± 4.5  Young's Modulus (MPa) 15.41 ± 0.84  12.88 ± 0.88  13.60 ± 0.63  13.87 ± 0.68  25% Secant Modulus (mPa) 5.97 ± 0.25 5.65 ± 0.19 5.77 ± 0.13 5.78 ± 0.13 100% Secant Modulus (mPa) 4.84 ± 0.26 5.06 ± 0.16 5.07 ± 0.28 4.96 ± 0.13

TABLE 3 INGREDIENT EX. 8 EX. 9 EX. 10 PBMA 83.98 79.87 77.95 PDMS (M_(n) 550-700) 2.01 4.09 5.94 PEG (1000) DMA 12.99 15.04 15.06 EGDMA 1.02 1.00 1.05 Appearance Clear Clear Clear (uncured liquid formulation) Appearance (dry) Clear Clear Clear Tackiness by handling Slightly tacky Tacky Tacky Conclusion Suitable for Unsuitable for Unsuitable for optical uses optical uses optical uses

EXAMPLES 11 AND 12 Monosubstituted polydimethylsiloxane (methylacryloxypropyl-terminated polydimethylsiloxane) (“Monosubstituted PDMS”)

The formulations shown below in Table 4 were prepared using the procedure described in Examples 4-7 above. Unlike the dimethylacryloxypropyl-terminated polydimethylsiloxane of the present invention, mono-substituted polydimethylsiloxane did not produce clear, reduced tack materials suitable for use as IOL materials.

TABLE 4 INGREDIENT EX. 11 EX. 12 PBMA 83.97  83.87  Monosubstituted PDMS — 2.13 (M_(n) 800-1200) Monosubsituted PDMS 2.02 — (M_(n) 4K-6K) PEG (1000) DMA 12.99  12.98  EGDMA 1.02 1.02 Appearance Cloudy Clear (uncured liquid formulation) (micellar mixture) Appearance (dry) Not cured Hazy after curing Tackiness by handling Not applicable Slightly tacky Conclusion Unsuitable for Unsuitable for optical uses optical uses 

1. A polymeric ophthalmic or otorhinolaryngological device material comprising a) a principal device-forming monomer which is an aryl acrylic hydrophobic monomer of the formula

wherein: A is H, CH₃, CH₂CH₃, or CH₂OH; B is (CH₂)_(m) or [O(CH₂)₂]_(n); C is (CH₂)_(w); m is 2-6; n is 1-10; Y is nothing, O, S, or NR, provided that if Y is O, S, or NR, then B is (CH₂)_(m); R is H, CH₃, C_(n)H_(2n+1)(n=1-10), iso-OC₃H₇, C₆H₅, or CH₂C₆H₅; w is 0-6, provided that m+w≦8; and D is H, C₁-C₄alkyl, C₁-C₄ alkoxy, C₆H₅, CH₂C₆H₅ or halogen, b) a dimethylacryloxypropyl-terminated polydimethylsiloxane macromer in an amount effective to reduce the tack of the polymeric ophthalmic or otorhinolaryngological device material, wherein the dimethylacryloxypropyl-terminated polydimethylsiloxane macromer has the formula

wherein R₁ and R₂ are independently —CH₃, —CH₂CH₃, —CH₂CH₂CH₂CH₃, CH₂CH₂CH₂CH₃, —C₆H₅, —CH₂C₆H₅, —CH₂CH₂C₆H₅, —CH₂CH₂CH₂C₆H₅, or —CH₂CH₂CH₂CH₂C₆H₅; R₃ is H, CH₃, or CH₂CH₃; z is 2-11; and x indicates the number of repeating units and is such that the macromer has a molecular weight of about 300-about 3500; and c) a cross-linking monomer, wherein the single device-forming monomer is present in an amount of at least about 75% (w/w).
 2. The polymeric ophthalmic or otorhinolaryngological device material of claim 1 wherein A is CH₃, B is (CH₂)_(m), m is 2-5, Y is nothing or O, w is 0-1, and D is H.
 3. The polymeric ophthalmic or otorhinolaryngological device material of claim 2 wherein the aryl acrylic hydrophobic monomer is selected from the group consisting of 4-phenylbutyl methacrylate; 5-phenylpentyl methacrylate; 2-benzyloxyethyl methacrylate; and 3-benzyloxypropyl methacrylate.
 4. The polymeric ophthalmic or otorhinolaryngological device material of claim 1 further comprising one or more components selected from the group consisting of reactive UV absorbers and reactive blue-light absorbers.
 5. The polymeric ophthalmic or otorhinolaryngological device material of claim 1 wherein the dimethylacryloxypropyl-terminated polydimethylsiloxane macromer is present in an amount from 0.5-3.9% (w/w).
 6. The polymeric ophthalmic or otorhinolaryngological device material of claim 5 wherein the dimethylacryloxypropyl-terminated polydimethylsiloxane macromer is present in an amount from 0.5-2% (w/w).
 7. The polymeric ophthalmic or otorhinolaryngological device material of claim 6 wherein the dimethylacryloxypropyl-terminated polydimethylsiloxane macromer is present in an amount from 0.8-1.2% (w/w).
 8. The polymeric ophthalmic or otorhinolaryngological device material of claim 5 wherein R₁═R₂═CH₃; R₃ is H, CH₃, or CH₂CH₃; z=3; and x=0-22.
 9. The polymeric ophthalmic or otorhinolaryngological device material of claim 8 wherein x=5-14.
 10. The polymeric ophthalmic or otorhinolaryngological device material of claim 8 wherein x=2-5.
 11. The polymeric ophthalmic or otorhinolaryngological device material of claim 1 wherein the material is an ophthalmic device material and has a refractive index of at least 1.50.
 12. The polymeric ophthalmic or otorhinolaryngological device material of claim 1 wherein the material has a Tg less than about +15° C.
 13. The polymeric ophthalmic or otorhinolaryngological device material of claim 1 wherein the material has an elongation of at least 90%.
 14. The polymeric ophthalmic or otorhinolaryngological device material of claim 1 wherein the cross-linking component comprises one or more cross-linking agents selected from the group consisting of ethylene glycol dimethacrylate; diethylene glycol dimethacrylate; allyl methacrylate; 1,3-propanediol dimethacrylate; 2,3-propanediol dimethacrylate; 1,6-hexanediol dimethacrylate; 1,4-butanediol dimethacrylate; CH₂═C(CH₃)C(═O)O—(CH₂CH₂O)_(p)—C(═O)C(CH₃)═CH₂ where p=1-50; CH₂═C(CH₃)C(═O)O(CH₂)_(t)OC(═O)C(CH₃)═CH₂ where t=3-20; and their corresponding acrylates.
 15. The polymeric ophthalmic or otorhinolaryngological device material of claim 1 wherein the single device-forming monomer is present in an amount of at least about 80% (w/w).
 16. The polymeric ophthalmic or otorhinolaryngological device material of claim 1 wherein the cross-linking monomer is present in an amount of about 0.01-17% (w/w).
 17. The polymeric ophthalmic or otorhinolaryngological device material of claim 1 wherein the aryl acrylic hydrophobic monomer is selected from the group consisting of 4-phenylbutyl methacrylate; 5-phenylpentyl methacrylate; 2-benzyloxyethyl methacrylate;and 3-benzyloxypropyl methacrylate; and the cross-linking monomer is CH₂═C(CH₃)C(═O)O—(CH₂CH₂O)_(p)—C(═O)C(CH₃)═CH₂, where p is such that the number average molecular weight of the cross-linking monomer is about
 1000. 18. An intraocular lens optic comprising the polymeric device material of claim
 1. 19. A device comprising the device material of claim 1 wherein the device is selected from the group consisting of a contact lens; a keratoprosthesis, a corneal inlay or ring; an otological ventilation tube; and a nasal implant. 